Leghe di nichel
Compositi bimetallici
Specifiche tecniche complete
- Centrifugal forces up to 100G eliminate porosity — density 15–25% higher than static castings
- Impurities self-segregate to inner bore and are machined away — clean outer structure guaranteed
- Bimetal composite capability: combine steel, bronze, nickel alloys in a single component
- Excellent radial mechanical properties — tensile strength and fatigue resistance superior to sand casting
- Weight range 1kg to 2,000kg — diameters from 50mm to 2,000mm achievable
- Cost-effective for cylindrical and tubular shapes — no cores, minimal gating waste
Parametri di processo completi per la colata centrifuga — basati sulle norme ISO 8062 / GB/T 6414.
Dimensional Tolerance
±0.5mm to ±1.5mm (OD)
Surface Finish
Ra 6.3–12.5μm (machined: Ra 0.8–1.6μm)
Typical Weight Range
1kg – 2000kg
Tolerance Grade
CT7-CT9
Parametro
Valore / Intervale
Note
Grado di tolleranza (ISO 8062)Toleranza OD; foratura lavorata per una tolleranza più strettaTolleranza dimensionale (OD)±0,5 mm – ±1,5 mmDipende dal diametro e dalla legaRuosità della superficie (Ra)6,3 – 12,5 μm in colataForatura lavorata: Ra 0,8–1,6 μm raggiungibile
Gamma di diametri
50 mm – 2.000 mmMacchine centrifughe orizzontali e verticaliGamma di peso tipica1 kg – 2.000 kgTubi di grandi dimensioni e vasi a pressioneForza centrifugaFino a 100G
Trascina impurità al foratura interno per la rimozione
Materiali tipici vasi a pressione
| Componenti rotativi e tubulari | Miglioramento della densità | 15–25% superiore alla colata statica |
|---|---|---|
| Le impurità si segregano dal foro lavorato | CT7 – CT9 | NDT / Ispezione |
| Dimensional Tolerance (OD) | ±0.5 mm – ±1.5 mm | Depends on diameter and alloy |
| Surface Roughness (Ra) | 6.3 – 12.5 μm as-cast | Machined bore: Ra 0.8–1.6 μm achievable |
| Diameter Range | 50 mm – 2,000 mm | Horizontal and vertical centrifugal machines |
| Typical Weight Range | 1 kg – 2,000 kg | Large pipes and pressure vessels |
| Centrifugal Force | Up to 100G | Drives impurities to inner bore for removal |
| Typical Materials | Gray iron, ductile iron, steel, SS, copper alloys, nickel alloys | Bimetal composites available |
| Bimetal Capability | Steel outer / Bronze inner | Sequential pouring of two alloys |
| Typical Applications | Pipes, cylinder liners, bearing rings, bushings, pressure vessels | Rotary and tubular components |
| Density Improvement | 15–25% higher than static casting | Impurities segregate to machined bore |
| NDT / Inspection | UT, MT, CMM report dimensionale | Test di pressione idrostatica disponibile |
| Tempo di consegna (produzione) | 20 – 40 giorni lavorativi | Dipende dal diametro e dalla quantità |
* Tutti i valori sono indicativi. I parametri effettivamente raggiungibili dipendono dalla geometria della parte, dalla lega e dalla progettazione degli utensili. Contatta i nostri ingegneri per una valutazione specifica del disegno.