Leghe di cobalto
Acciaio duplex
Specifiche tecniche complete
- Dimensional tolerances as tight as ±0.1mm — CT4 to CT6 grade achievable
- Surface finish Ra 1.6–3.2μm directly from casting — reduces or eliminates machining
- Complex geometries: undercuts, thin walls (down to 1.5mm), internal passages in one piece
- Broad material range: carbon steel, 304/316 stainless, titanium Ti-6Al-4V, Inconel 718, cobalt alloys
- Near-net-shape output — material utilization typically 85–95%, reducing waste and cost
- Consistent quality from prototype to 50,000+ piece production runs
Parametri di processo completi per la colata per investimenti — basati sulle norme ISO 8062 / GB/T 6414.
Dimensional Tolerance
±0.1mm to ±0.3mm
Surface Finish
Ra 1.6–6.3μm
Typical Weight Range
0.01kg – 50kg
Tolerance Grade
CT4-CT6
Parametro
Valore / Gamma
Note
Grado di tolleranza (ISO 8062)Realizzabile su geometrie aerospaziali complesseToleranza dimensionale±0,1 mm – ±0,3 mmDipende dalle dimensioni della parte e dalla legaRuggitudine della superficie (Ra)1,6 – 6,3 μmAs-cast; 0,8 μm raggiungibile dopo lavorazione
Spessore minimo della parete
1,5 mmCapacità a parete sottile con porta ottimizzataGamma di peso tipica0,01 kg – 50 kgParti più pesanti su richiestaMateriali tipiciAcciaio al carbonio, 304/316 SS, Ti-6Al-4V, Inconel 718, Leghe di cobalto
Elenco completo delle leghe su richiesta
Applicazioni tipiche
| Lame di turbine, giranti, corpi valvole, impianti medici, staffe aerospaziali | Trattamento termico | Recucimento, normalizzazione, estinzione e temperamento, soluzione + invecchiamento AS9100D su richiesta |
|---|---|---|
| Certificazioni di materiale (MTR) incluse | CT4 – CT6 | Tempo di consegna (prototipo) |
| 15 – 25 giorni lavorativi | Dal disegno approvato al primo articolo | Depends on part size and alloy |
| Surface Roughness (Ra) | 1.6 – 6.3 μm | As-cast; 0.8 μm achievable after machining |
| Minimum Wall Thickness | 1.5 mm | Thin-wall capability with optimised gating |
| Typical Weight Range | 0.01 kg – 50 kg | Heavier parts on request |
| Typical Materials | Carbon steel, 304/316 SS, Ti-6Al-4V, Inconel 718, Cobalt alloys | Full alloy list on request |
| Typical Applications | Turbine blades, impellers, valve bodies, medical implants, aerospace brackets | — |
| Heat Treatment | Annealing, normalising, quench & temper, solution + aging | Per ASTM / AMS specifications |
| NDT / Inspection | X-ray, PT, MT, UT, CMM dimensional report | Third-party inspection available |
| Certifications | ISO 9001:2015; AS9100D on request | Material certs (MTR) included |
| Lead Time (prototype) | 15 – 25 working days | From approved drawing to first article |
| Tempo di consegna (produzione) | 25 – 45 giorni lavorativi | Dipende dalla quantità e dalla complessità |||SEP|| * Tutti i valori sono indicativi. I parametri effettivamente raggiungibili dipendono dalla geometria della parte, dalla lega e dalla progettazione degli utensili. Contatta i nostri ingegneri per una valutazione specifica del disegno. |
Esplora altri processi
Hai bisogno di lavorazione CNC di precisione dopo la colata?
Add-On Service
Offriamo soluzioni integrate chiavi in mano Casting+CNC. Un fornitore, un contratto, una garanzia di qualità - dalla colata grezza alla parte finita e pronta per l'assemblaggio.
Casting+CNC chiavi in mano → ||| SEP||| Visualizza le capacità CNC → ||| Pronto a iniziare il tuo progetto di Fusione a cera persa? Carica il tuo disegno e ricevi una recensione di ingegneria esperta entro 24 ore. PrimeCast Global