Ejes de hélices marinas
Cojinetes bimetales
Materiales compatibles
- Centrifugal forces up to 100G eliminate porosity — density 15–25% higher than static castings
- Impurities self-segregate to inner bore and are machined away — clean outer structure guaranteed
- Bimetal composite capability: combine steel, bronze, nickel alloys in a single component
- Excellent radial mechanical properties — tensile strength and fatigue resistance superior to sand casting
- Weight range 1kg to 2,000kg — diameters from 50mm to 2,000mm achievable
- Cost-effective for cylindrical and tubular shapes — no cores, minimal gating waste
Hierro gris
Dimensional Tolerance
±0.5mm to ±1.5mm (OD)
Surface Finish
Ra 6.3–12.5μm (machined: Ra 0.8–1.6μm)
Typical Weight Range
1kg – 2000kg
Tolerance Grade
CT7-CT9
Hierro dúctil
Acero
Acero inoxidable
Aleaciones de cobreAleaciones de níquelComposites bimetalesEspecificaciones técnicas completasParámetros de proceso completos para fundición centrífuga — basados en las normas ISO 8062 / GB/T 6414.ParámetroValor / RangoNotas
Grado de tolerancia (ISO 8062)
Tolerancia OD; taladro mecanizado a una tolerancia más cercanaTolerancia dimensional (OD)±0.5 mm – ±1.5 mmDepende del diámetro y la aleaciónRugosidad de la superficie (Ra)6.3 – 12.5 μm como fundidotaladro mecanizado: Ra 0.8–1.6 μm alcanzable
Rango de diámetro
50 mm – 2.000 mm
| Máquinas centrífugas horizontales y verticales | Rango de peso típico | 1 kg – 2.000 kg |
|---|---|---|
| Tubos grandes y recipientes a presión vasos a presión | CT7 – CT9 | Componentes rotativos y tubulares |
| Mejora de la densidad | 15–25% más alto que la fundición estática | Las impurezas se segregan al taladro mecanizado |
| NDT / Inspección | 6.3 – 12.5 μm as-cast | Machined bore: Ra 0.8–1.6 μm achievable |
| Diameter Range | 50 mm – 2,000 mm | Horizontal and vertical centrifugal machines |
| Typical Weight Range | 1 kg – 2,000 kg | Large pipes and pressure vessels |
| Centrifugal Force | Up to 100G | Drives impurities to inner bore for removal |
| Typical Materials | Gray iron, ductile iron, steel, SS, copper alloys, nickel alloys | Bimetal composites available |
| Bimetal Capability | Steel outer / Bronze inner | Sequential pouring of two alloys |
| Typical Applications | Pipes, cylinder liners, bearing rings, bushings, pressure vessels | Rotary and tubular components |
| Density Improvement | 15–25% higher than static casting | Impurities segregate to machined bore |
| NDT / Inspection | UT, MT, CMM informe dimensional | Prueba de presión hidrostática disponible |
| Tiempo de entrega (producción) | 20 – 40 días laborables | Depende del diámetro y la cantidad |
* Todos los valores son indicativos. Los parámetros reales alcanzables dependen de la geometría de la pieza, la aleación y el diseño de las herramientas. Póngase en contacto con nuestros ingenieros para la evaluación específica del dibujo.