Specifiche tecniche complete
Parametri di processo completi per la colata di schiuma perduta — basati sulle norme ISO 8062 / GB/T 6414.
Parametro
- Complex integrated structures in one piece — eliminates 3–5 separate components and assembly welding
- No sand cores required — internal passages and undercuts formed directly by foam pattern
- CT7–CT9 dimensional tolerance — better than conventional sand casting for complex shapes
- Reduced machining allowance: 2–3mm typical versus 5–8mm for green sand casting
- Design freedom: wall thickness down to 4mm, internal passages, re-entrant angles all achievable
- Total cost reduction of 20–40% versus multi-component fabricated alternatives
Valore / Gamma
Dimensional Tolerance
±0.5mm to ±1.0mm
Surface Finish
Ra 6.3–12.5μm
Typical Weight Range
1kg – 500kg
Tolerance Grade
CT7-CT9
Note
Grado di tolleranza (ISO 8062)
Migliore rispetto alla fusione di sabbia verde convenzionale
Toleranza dimensionale±0,5 mm – ±1,0 mmDipende dalle dimensioni della parte e dalla qualità della schiumaRuosità della superficie (Ra)6,3 – 12,5 μmMigliorato con qualità del rivestimento refrattarioSpessore minimo della parete4,0 mm
Passaggi interni e sottotagli realizzabili
Gamma di peso tipica ||| case di pompa complesseStrutture integrate a cavità multipleRequisiti fondamentaliNessun nucleo di sabbia necessarioPassaggi interni formati da schiuma
Permessa di lavorazione
2 – 3 mm
| rispetto a 5-8 mm per la colata di sabbia verde | Vantaggio sui costi | Costo totale inferiore del 20-40% |
|---|---|---|
| rispetto alle alternative fabbricate a più componenti | CT7 – CT9 | Better than conventional green sand casting |
| Dimensional Tolerance | ±0.5 mm – ±1.0 mm | Depends on part size and foam pattern quality |
| Surface Roughness (Ra) | 6.3 – 12.5 μm | Improved with refractory coating quality |
| Minimum Wall Thickness | 4.0 mm | Internal passages and undercuts achievable |
| Typical Weight Range | 1 kg – 500 kg | Large complex structures in one piece |
| Typical Materials | Gray iron, ductile iron, carbon steel, SS, aluminum alloys | Most ferrous and non-ferrous alloys |
| Typical Applications | Engine blocks, cylinder heads, intake manifolds, complex pump housings | Multi-cavity integrated structures |
| Core Requirements | No sand cores needed | Internal passages formed by foam pattern |
| Machining Allowance | 2 – 3 mm | vs. 5–8 mm for green sand casting |
| Cost Advantage | 20–40% lower total cost | vs. multi-component fabricated alternatives |
| NDT / Ispezione | Rapporto dimensionale a raggi X, UT, CMM | Ispezione di terze parti disponibile |
| Tempo di consegna (produzione) | 30 – 50 giorni lavorativi | Utensili in schiuma inclusi |
* Tutti i valori sono indicativi. I parametri effettivamente raggiungibili dipendono dalla geometria della parte, dalla lega e dalla progettazione degli utensili. Contatta i nostri ingegneri per una valutazione specifica del disegno.